High Alumina Runner Ingot Bricks Introduction

The high temperature physical and chemical properties of high alumina runner ingot fire brick are relatively good in the same kind of refractory products. High alumina runner ingot fire brick are resistant to erosion, no deformation, no falling off, high refractoriness, good chipping resistance and strong corrosion resistance. Regular, the ramp is smooth, the dimensions are precise, and the seams are tight. High alumina runner ingot refractory brick has a huge demand is widely used steel smelting. 

High Alumina Runner Ingot Bricks Features

1. Fireproof alumina runner ingot brick has high refractoriness and good physical and chemical properties at high temperature.

2. Refractory alumina runner ingot brick has good crack resistance and erosion resistance.

3. Alumina runner ingot bricks has resistant to erosion, no deformation and no falling off.

High Alumina Runner Ingot Bricks Specification

Modle/item	Fire-clay		High Alumina				andalusite
	FC-36	FC-40	HL-48	HL-55	HL-65	HL-70
Al2O3 %	>36	>40	>48	>55	>65	>70	>57
Fe2O3 %	<2.0	<1.8	<2.0	<2.0	<2.0	<1.5	<2.0
Alkaline %	<1.8	<1.8	<1.8	<1.8	<1.8	<1.8	/
Apparent porosity %	17-25	<22	<25	<26	<26	<25	<25
Bulk Density g/cm3	>2.1	>2.18	>2.2	>2.25	>2.3	>2.35	>2.30
Refractoriness ℃	>1700	>1710	>1750	>1770	>1790	>1790	>1790

 
High Alumina Runner Ingot Bricks Applications

1. Fire brick application in glass kiln.

2. Refractory brick is suitable in ceramic tunnel kiln.

3. Refractory brick is suitable in Iron making furnaces.

4.High alumina runner ingot bricks is used in the cement kiln.

5. Refractory runner ingot bricks is widely used in steel furnaces.

High Alumina Runner Ingot Bricks Customized in RongSheng Refractory

Rongsheng reractory factory offers fire clay, high alumina, alumina-silica and other customized refractory materials in the manufacturing of the hollow wares. 

Rongsheng offers a typical set of hollow wares consist of the following shapes for ingot casting of steel industry

 
1.Funnel or Trumpet - Bell Bricks 

2.Long ,Round Stack Bricks

3.Short, Round Stack Bricks

4.Bottom Guide Bricks 

5.Spider or Center Runner Bricks( 1-way through 8-way) 

6.Long, Square Runner Bricks

7. Short, Square Runner Bricks

8.End Gate Bricks 

10.Center Riser Bricks

Other refractory bricks shape and sizes are available based on the specific requirements of the customers
 
 

High Alumina Runner Ingot Bricks Manufacturer in Rongsheng Refractory

High alumina runner ingot bricks manufacturer in RongSheng refractory brick factory, Rongsheng Refractory Group provide competitive price and high quality of high alumina runner ingot bricks.

Rongsheng refractory factory have a strong technical team, including the kiln construction team on-site guidance technical team and R & D team and research team and major universities jointly set up to solve various high requirements of customers. Testing team professional testing team, according to the physical and chemical indicators of refractory materials, refractory material is tested whether it meets the requirements of customers.

Graphite Electrode URP

Graphite Electrode URP Definition

Ultra high power graphite electrodes (EHSP-UHP) are manufactured for operation at currents with a density of more than 25A / cm2

Graphite Electrode URP Application

1.URP graphite electrode used in steel making electric arc furnaces, refining furnaces, as conductive electrodes.

2.Graphite electrode URP used in industrial silicon furnaces, yellow phosphorus furnaces, corundum furnaces. As conductive electrodes for graphite electrode URP.

Graphite Electrode UHP Specification
 

Name	Unit	diameter of electrode 300mm-600mm
		standard		Actual measurement
		Electrode	Nipple	Electrode	Nipple
Specific electrical resistivity	μOhm • m	6.2-6.5	5.5	5.0-6.5	4.5
Limit of mechanical resistance to bending	MPa	10.5	16	14-16	18-20
Elastic modulus	GPa	14	18	12	14
Ash content, not more than	%	0.5	0.5	0.5	0.5
Bulk density, not less than	g / cm3	1.64-1.65	1.70-1.72	1.72-1.75	1.78
Thermal coefficient of linear expansion (100-600 ° C)	× 10-6 / ℃	1.5	1.4	1.3	1.2

 
The Length & Diameter & Permissible Deviation of the Graphite Electrode UHP
 

Diameter				Length
Nominal diameter		Actual diameter		Nominal length	tolerance
Millimeters (mm)	Inch (inch)	Max. (Max.)	Min (min)	mm	Length	the maximum
300	12	307	302	1600 1800	± 100	-100	-275
350	14	357	352
400	16	409	403
450	18	460	454
500	20	511	505	1600/1800/2000/2200	± 100	-100	-275
550	22	556	553
600	24	613	607

 
Graphite Electrode UHP Current Capacity
 

Nominal diameter		Current throughput (A)	The current density (A / cm2)
Millimeters (mm)	Inch (inch)
250	10	9200-15100	21-30
300	12	13000-22000	20-30
350	14	20000-30000	20-30
400	16	25000-40000	19-30
450	18	32000-45000	19-27
500	20	38000-55000	18-27
550		48000-60000	18-24
600	24	52000-72000	18-24
700	27th	62000-95000	18-24

Graphite Electrode URP Manufacturer in RS Refractory Factory Advantages

1.High quality graphite electrodes products.

2.Graphite electrode URP manufacturer from China

3.Profitable price for high quality graphite electrodes.

4.RS refractory factory can produce various specifications in accordance with customer requirements.
 
Graphite Electrode URP Using Precautions 

1.In actual use the graphite electrode URP, specifications and grades of the graphite electrode should be selected according to the specific furnace conditions.

2.Primary factor is the maximum current intensity, but also consider the influence of other factors, such as the characteristics of the Arc electric furnace itself, the type of charge, the smelting time, the oxygen blowing amount, the mechanical requirements, the steel making process.

3. Normally, specification of most grades of graphite electrodes have been standardized. But in the process of use, sometimes also consider the temperature to some impacts of these indicators.

4. Select the grade and diameter of the electrode according to the furnace capacity and transformer load.

5. When charging the electric furnace, refractory material should be installed at the bottom of  furnace to prevent furnace refractory material from collapsing and breaking the electrode. In the smelting process, lime, it should be avoided.

6. A large amount of objects are concentrated directly under the electrodes, otherwise it will affect the energization of the electrodes and may even cause the electrodes to break.

7. Pay attention to the position of the furnace cover. If the furnace cover is misaligned, the furnace cover will be scratched when the electrode is lifted, resulting in damage to the electrode.

8. If the connector plug is found to be missing when connecting the electrode, replace it and connect it.

9. After the electrodes are connected, if there is a gap on the connection surface, be sure to find out the cause. It can be used after the gap is eliminated.

10. Graphite electrode holder should be sandwiched between the upper and lower guard lines of the topmost electrode. It is forbidden to be caught in the warning line (the joint hole) and the middle electrode, otherwise the electrode column may be broken.

11.Since raw refractory materials and production processes of different manufacturers may be different, the physical and chemical properties of the electrodes are also different. It is recommended that the joints and electrodes produced by different manufacturers should not be used interchangeably during use.